Title :   DETERMINATION OF THE RATE OF DIFFUSION OF HYDROGEN THROUGH 1KH18N9T STEEL AT HIGH TEMPERATURES AND PRESSURES

Corporate Author : FOREIGN TECHNOLOGY DIV WRIGHT-PATTERSON AFB OHIO

Personal Author(s) : ARCHAKOV,YU. I. ; GREBESHKOVA,I.D. ; TEODOROVICH,V.P.

Report Date : 27 JUL 1961

Pagination or Media Count : 1

Abstract : A method was developed for determining the rate of diffusion of H through various steels at high temperatures and pressures. The principal feature of the method was the avoidance of welded joints on the computational surface of the metal through which the gas diffuses. The rate of diffusion of H through 1Kh18N9T steel was studiedAT 500 C with H pressures to 300 kg/sq cm, at 600 to 800 C and pressures to 200 kg/sq cm, at 900 C and 100 kg/sq cm, at 950 C and 75 kg/sq cm and at 1000 C and 50 kg/sq cm on 6 tubular samples. The difference in the values of the rate of diffusion during the testing of various samples did not exceed ! 5%. There was a parabolic dependence between the rate of H diffusion and the H pressure within the tubular sample. (Author)

Descriptors :   *DIFFUSION, *HYDROGEN, DETERMINATION, HIGH PRESSURE, HIGH TEMPERATURE, MEASUREMENT, STEEL, TEST EQUIPMENT, TEST METHODS

Distribution Statement : APPROVED FOR PUBLIC RELEASE