Accession Number : AD0477449

Title :   DEVELOPMENT OF TOUGH, HIGH STRENGTH ALPHA BETA TITANIUM-BASE ALLOYS AT 240,000-260,000 PSI YIELD STRENGTH LEVEL.

Descriptive Note : Quarterly progress rept. no. 11, 26 Dec 64-15 Mar 65,

Corporate Author : NEW YORK UNIV BRONX SCHOOL OF ENGINEERING AND SCIENCE

Personal Author(s) : Farrar, P. A. ; Margolin, H.

Report Date : DEC 1965

Pagination or Media Count : 24

Abstract : In order to develop titanium alloys with higher ductilities and 0.1% yield strengths in the range of 190,000 to 240,000 psi and usable ductility in the range from 240,000 to 260,000 psi, a total of 53 eight-pound ingots were investigated. An additional 3 eight-lb. iodide Ti base ingots are being prepared. Four alloys which showed promising properties in the 190,000-240,000 psi range as 8-lb. ingots were remelted as 80-lb. ingots for further evaluation as bar, plate and sheet material. Tensile tests at room temperature and -40 F impact tests were completed on the bar stock and the plate for the four ingots, and welding tests were conducted on the sheet material. Elevated and low temperature tests on the bar stock were completed and the data are included. The compositions of four additional alloys to be evaluated as 80-lb. ingots were selected and preparation of the ingots was begun. (Author)

Descriptors :   (*TITANIUM ALLOYS, PROCESSING), ALUMINUM ALLOYS, TIN ALLOYS, VANADIUM ALLOYS, IRON ALLOYS, COPPER ALLOYS, ZIRCONIUM ALLOYS, CARBON ALLOYS, CHROMIUM ALLOYS, NICKEL ALLOYS, MOLYBDENUM ALLOYS, PREPARATION, TOUGHNESS, DUCTILITY, ADDITIVES, CARBON, OXYGEN, BORON.

Subject Categories : Metallurgy and Metallography