Accession Number : AD0775238

Title :   An Electron Microscopic Examination of Pre-Crack Fatigue Damage in Age Hardened Al 5.0 Zn 2.5 Mg.

Descriptive Note : Technical rept.,

Corporate Author : RENSSELAER POLYTECHNIC INST TROY N Y MATERIALS DIV

Personal Author(s) : Duquette,David J. ; Swann,Peter R.

Report Date : FEB 1974

Pagination or Media Count : 31

Abstract : High cycle bending fatigue tests were performed on sheet specimens of an Al, 5.0 w/o Zn, 2.5 w/o Mg alloy. Electron microscopic observations of the free surfaces of the alloy sheets were performed on specimens cycled to crack initiation. These observations showed that low strain fatigue results in the generation of screw dislocations in the vicinity of surface connected grain boundary triple points. As cycling continues, these screw dislocations form jogs which are subsequently pinched off to form sessile edge dislocation loops. It is suggested that crack initiation occurs at a critical dislocation loop density in very narrow slip bands, and that the initiation step is affected by a normal component of stress across the slip plane as a result of dislocation dipole interaction. This normal stress results in a localized cleavage type of failure associated with Stage I cracking in high strength precipitation hardened alloys. (Modified author abstract)

Descriptors :   *Fatigue(Mechanics), *Aluminum alloys, Crack propagation, Electron microscopy, Dislocations, Age hardening, Magnesium alloys, Zinc alloys

Subject Categories : Metallurgy and Metallography

Distribution Statement : APPROVED FOR PUBLIC RELEASE