Title :   Glass Fibre/Epoxy Resin Interface Life-Time Prediction.

Descriptive Note : Final rept. Apr 81-Apr 83,

Corporate Author : BRISTOL UNIV (ENGLAND) H H WILLS PHYSICS LAB

Personal Author(s) : Ashbee,K H G ; Hoeel,R ; Sargent,J P ; Walter,Elizabeth

PDF Url : ADA132206

Report Date : Apr 1983

Pagination or Media Count : 48

Abstract : Chemical reaction, adsorption and diffusion in polymers are all enhanced by stress and, as is the case for other materials, localized stresses, since they initiate failures, are more important than overall levels of residual stress. The solutions contained inside interfacial pressure pockets are corrosive and their destructive action, on the bonds responsible for load transfer, is enhanced by residual interfacial stress. There exist no high resolution techniques for measuring localized deformation in non-crystalline materials. In crystals, however, local elastic strain can be detected and measured using Kossel X-ray diffraction and electron beam back scattering diffraction in the SEM, and convergent beam diffraction in the TEM. Each of these facilities has been used to study residual stress close to a-quartz/epoxy resin interfaces in order to establish the general nature and magnitude of interfacial stress in SiO2/epoxy composite materials including GRP. At 40mm from the interface local strain is 2%. The corresponding large interfacial stresses are held responsible for the observed very strong dependence of mechanical damping on interfacial area.

Descriptors :   *Glass reinforced plastics, *Epoxy resins, *Interfaces, *Crack propagation, Loads(Forces), Osmotic pressure, Fracture(Mechanics), Water, Stress corrosion, Fiber reinforced composites, Nondestructive testing, Predictions, Cracking(Fracturing)

Subject Categories : Laminates and Composite Materials
      Test Facilities, Equipment and Methods
      Mechanics

Distribution Statement : APPROVED FOR PUBLIC RELEASE