Title :   Analyses of Surface Cracks in Finite Plates Under Tension or Bending Loads.

Descriptive Note : Technical paper,

Corporate Author : NATIONAL AERONAUTICS AND SPACE ADMINISTRATION HAMPTON VA LANGLEY RESEARCH CEN TER

Personal Author(s) : Newman, J. C., Jr. ; Raju, I. S.

PDF Url : ADA303923

Report Date : DEC 1979

Pagination or Media Count : 46

Abstract : This paper presents stress-intensity factors calculated with a three-dimensional, finite-element analysis for shallow and deep semielliptical surface cracks in finite elastic isotropic plates subjected to tension or bending loads. A wide range of configuration parameters was investigated. The ratio of crack depth to plate thickness ranged from 0.2 to 0.8 and the ratio of crack depth to crack length ranged from 0.2 to 2.0. The effects of plate width on stress-intensity variations along the crack front were also investigated. A wide-range equation for stress-intensity factors along the crack front as a function of crack depth, crack length, plate thickness, and plate width was developed for tension and bending loads. The equation was used to predict patterns of surface-crack growth under tension or bending fatigue loads. A modified form of the equation was also used to correlate surface-crack fracture data for a brittle epoxy material within + or - lO percent for a wide range of crack shapes and crack sizes. (MM)

Descriptors :   *CRACK PROPAGATION, *EPOXY RESINS, STRESS ANALYSIS, ALUMINUM ALLOYS, FINITE ELEMENT ANALYSIS, LOADS(FORCES), TENSILE STRESS, CRACKS, ELASTIC PROPERTIES, BENDING, ALLOYS, FRACTURE(MECHANICS), SURFACES, DEFECTS(MATERIALS), BRITTLENESS, PLATES, ISOTROPISM, FATIGUE(MECHANICS).